Silicone Rubber for Concrete Stone Tile Mold Making (MCSIL-2066)
|FOB Price:||US $5.8 / kg|
|Min. Order:||200 kg|
|Min. Order||FOB Price|
|200 kg||US $5.8/ kg|
|Transport Package:||20kg/Drum, 25kg/Drum or 200kg/Drum|
|Payment Terms:||L/C, T/T|
- Model NO.: MCSIL-2066/2088 silicone rubber
- Material: Silicone Rubber
- Form: Liquid Silicone Rubber
- Color: off-White
- Hardness: 28-30 Shore a
- Elongation at Break: 420%
- Certification: MSDS,SGS,Reach
- Specification: REACH, MSDS, SGS
- HS Code: 39100000
- Raw Material: Silicone Raw Material
- Appearance: Liquid
- Item: Mcsil-2066
- Mixing Ratio: 100:2
- Tensile Strength: 3.8 MPa
- Sample: Free
- Trademark: MC SILICONE
- Origin: Dongguan, China
Silicone Rubber for Concrete Stone Tile Mold Making (MCSIL-2066) is a kind of two-component material, that is the moldmaking silicone rubber is made up of Part A base silicone and Part B CA30 curing agent. The mixed Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction, and the become a siliconer rubber mold that can be used for objects reproduction. These RTV-2 silicone rubber molds can be cast into different material for your target objects. The pouring material can be plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...
Specifications of Silicone Rubber for Concrete Stone Tile Mold Making (MCSIL-2066)
Equiped with REACH certificate
Professional technician with rich experience
4% catalyst is offered for free of charge
Silicone range: 10-60 shore A
High duplicating silicone molds
Applications of Silicone Rubber for Concrete Stone Tile Mold Making (MCSIL-2066)
RTV Silicone Rubber for concrete mold making is suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc
Instructions for Making Concrete Silicone Molds
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Shortage of Silicone Rubber for Concrete Stone Tile Mold Making (MCSIL-2066)
When the RTV silicone rubber for concrete mold making is stored at or below 30 ° C(85 ° F) in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production. After 12 months, please use a stirring mill to stir the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
FAQ of Silicone Rubber for Concrete Stone Tile Mold Making (MCSIL-2066)
Why does the RTV liquid silicone rubber for molding have few mold making times?
The silicone rubber mold has few molding times is due to follwoing reasons: Adding too much silicone oil which will destroy the molecular of silicone rubber; Making the mold for small and fine detailed products with higher hardness silicone rubber which is easy to break; Making the mold for large products with soft silicone rubber which will reduce the tensile and tear strength of the mold, and the mold will have deformation. Thus, we should take the proper silicone rubber to make the mold for suitable products.
Need more information, please feel free to contact me.
|Hardness||28-30 Shore A|
|Tear Strength||27 N/mm|
|Tensile Strength||≥3.8 Mpa|
|Relative density||1.09-1.15 g/cm3|
|Elongation at break||420%|
Package of Silicone Rubber for Concrete Stone Tile Mold Making (MCSIL-2066)
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle and 1kg/bottle
Professional factory of RTV2 silicone:
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series, we are competitive in price with good quality.
Should you have any question, please feel free to contact us .