Description of Liquid Silicone Rubber for Candle Mold Making
Liquid silicone rubber is a two-component material, which consists of Part A base silicone and Part B CA30 curing agent; Then the silicone base and curing agent can cure at room temperature by a condensation reaction. These silicone rubber materials can be cast into the cured silicone mold: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc.
Specifications of Liquid Silicone Rubber for Candle Mold Making
1. Good flow ability and long working time
2. Low hardness, easy de-mold
3. High tear and tensile strength
4. Acid and alkali-resistance
5. Low linear shrinkage
Applications of Liquid Silicone Rubber
Liquid silicone rubber for mold making can be applied in many objects mold making, since MC liquid silicone rubber has good flow ability and medium hardness, and the silicone can cure at room temperature, thus it's a good material for duplication.
RTV-2 Silicone Rubber can be used for artificial stone mold making. For example MCSIL-2066 and MCSIL-2088 silicone.
RTV-2 silicone rubber can be applied in candle and soap mold making, such as MCSIL-215 and MCSIL-218 silicone.
RTV-2 silicone rubber can be used for plaster mold making, such as MCSIL-2025, MCSIL-H25 and MCSIL-2030 silicone.
RTV-2 silicone rubber can be applied in the field of shoe sole moldmaking, for example, MCSIL-S10 and MCSIL-S15 silicone.
RTV-2 silicone rubber can be used for prototyping and electronic potting.
MCSIL-215/218 silicone rubber is suited for middle size reproduction of candle mold, soap mold, small size concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, and the products with thin flower patterns.
Detail Standard of Liquid Silicone Rubber for Candle Mold Making
Base and Curing Agent Mixture (100: 2 by weight) in 25C (77F) testing
Item No. MCSIL-215
Applications Candle
ColorOff- white
Curing agentCA30
Mixing ratio100: 2
Mixed viscosity 18000-20000 cps
Pot life30-40 Minutes
Curing time 4-6 Hours
Hardness13-15 Shore A
Tear Strength24 N/mm
Tensile Strength3.5 MPA
Shrinkage0.30%
Elongation at break550%
How to make the silicone mold?
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Storage of Liquid Silicone Rubber for Candle Mold Making
When the silicone rubber is stored at or below 30C (85F) in the original unopened containers, silicone base and curing agent have a usable life of 12 months from the date of production.
Note of Liquid Silicone Rubber for Candle Mold Making
RTV2 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.
Packing of Liquid Silicone Rubber for Candle Mold Making
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle
Need more information, please feel free to contact Nicole.
| Item No. |
MCSIL-215 |
| Applications |
Candle/Soap Molding |
| Color |
Off- white |
| Curing agent |
CA30 |
| Mixing ratio |
100:2 |
| Mixed viscosity |
18000-20000 cps |
| Pot life |
30-40 Minutes |
| Curing time |
4-6 Hours |
| Hardness |
13-15 Shore A |
| Tear Strength |
24 N/mm |
| Tensile Strength |
3.5 MPA |
| Shrinkage |
0.30% |
| Elongation at break |
550% |