Platinum Cure High Transparent RTV Silicone Rubber

Raw Material: Silicone Rubber Raw Material
Material: Silicone Rubber
Appearance: Liquid
Form: Liquid Rubber
Item: Mcpla-H50
Color: Transparent/Clear
Customization:

Contact Supplier

Gold Member Since 2013

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
MCPLA-H50 Silicone rubber
Mixing Ratio
10:1
Mixed Viscosity
85000 Cps
Working Time
60 Mins
Curing Time
8 Hours
Hardness
50 Shore a
Tear Strength
25 N/Mm
Tensile Strength
5.8 MPa
Elongation at Break
350%
Transport Package
20kg/Drum, 25kg/Drum or 200kg/Drum
Specification
REACH, MSDS, SGS
Trademark
MC SILICONE
Origin
Dongguan, China
HS Code
39100000
Production Capacity
4000kg/Day

Product Description

Description of Platium Catalysted RTV-2 Silicone Rubber

RTV silicone rubber is a two component elastomeric cross-linking at room temperature. The polymerization can be accelerated by heat (max. 1500 C). The silicone components are delivered as liquids, which once mixed and cured transform into a transparent, elastic and resistant material. Polymerization occurs without formation of heat.

Advantages of Platium Catalysted RTV-2 Silicone Rubber

1. Easy Curing: MCPLA-H50 polymerizes at room temperature (23C). The curing characteristics is independent of part thickness.
2. Transparent appearance
3. High tear and tensile strength
4. Long shelf life with low shrinkage
5. Fast mixing (10: 1) and easy processing due to the low viscosity

Applications of Platium Catalysted RTV-2 Silicone Rubber

Label manufacturing, Molding applications requiring low shrinkage, such as toys, jewelers, automotive, rapid prototyping etc.

Technical datasheet of Platium Catalysted RTV-2 Silicone Rubber
Base and Curing Agent Mixture (100: 10 by weight) in 23 C (73F) testing

Item                                 MCPLA-H50
Color                               Clear
Mixing ratio                    100: 10
Mixed viscosity               85000 cps
Working time                  60 mins
Curing time                     8 Hours
Hardness                        50 Shore A
Tear Strength                  25 N/mm
Tensile Strength             ≥ 5.8 Mpa
Shrinkage                         ≤ 0.1%
Elongation at break        350%
Relative density              1.1 g/cm3

Instructions for making silicone molds

1. Mixing the two components
According the mixing ratio 10: 1 weighting part A and B, the two components may be thoroughly mixed either by hand or using a low speed electric to minimize the entrance of air and to avoid any temperature increase.
Note: It is also possible to use a special mixing and dispensing machine for the two silicone components, further information is available upon request.

2. Molding
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter/height ratio(3 to 4 times of the initial volume)

3. Polymerization
The curing may be slowed down at lower temperature or accelerated by applying heat.
Note: In general contact with certain materials can inhibit the cross linking of RTV.
Natural rubbers vulcanized with sulfur
RTV elastomeric is catalyzed with metal salts, e. G. Tin compounds
PVC stabilized with tin salts and additives
Epoxy catalyzed with amines
Certain organic solvents, such as Ketones, alcohols, ether etc.

In case of doubt, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.

Storage and shelf life of Platium Catalysted RTV-2 Silicone Rubber

Silicone RTV must be used within 6 months from the manufacturing date. Beyond this date, MC silicone no longer guarantees the products confirms with the sales specification. In order to preserve best properties it is recommended to follow strictly the following guidelines:
Store the original packing tightly sealed and at a temperature below 30 C
Use the product as soon as the packaging has been opened.

Packaging of Platium Catalysted RTV-2 Silicone Rubber

Part A: 20kg/drum; Part B: 2 kg /drum
Special containers are available are on request.

Need more information, please feel free to contact Nicole.
ItemMCPLA-H50
ColorClear
Curing agentCA30
Mixing ratio100:10
Mixed viscosity85000 cps
Working time 60 mins
Curing time 8  Hours
Hardness50 Shore A
Tear Strength25 N/mm
Tensile Strength≥5.8 Mpa
Shrinkage≤0.1%
Elongation at break350%
Relative density 1.1 g/cm3