9: 1 Mix Ratio Addition Cure RTV-2 Liquid Silicone Rubber Pad Printing Silicone

• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Appearance: Liquid
• Form: Liquid Rubber
• Item: Mc-P30
• Color: Reddish Brown(Translucent)
• Model NO.: MC-P30 silicone rubber
• Mixing Ratio: 9:1
• Mixed Viscosity: 10000 Cps
• Working Time: 30-35 Mins
• Curing Time: 4-6 Hours
• Hardness: 31-32 Shore a
• Tensile Strength: 7 MPa
• Tear Strength: 30n/mm
• Elongation at Break: 580%
• Shelf Life: 12 Months
• Transport Package: 20kg/Drum or 200kg/Drum
• Specification: REACH, MSDS, SGS
• Trademark: MC SILICONE
• Origin: Dongguan, China
• HS Code: 39100000
• Production Capacity: 2000kg/Day

Product Description

MCSIL-P30 A/B pad printing silicone rubber is a pourable, addition curing, two-component silicone rubber that vulcanizes at room temperature.pad printing silicone rubber is a base material for making printing pads.it is suited for pad printing of letters/patterns on plastic toys, electronic toys and parts, trademark, PVC toys, etc.


Advantages of RTV-2 Silicone Rubber for Pad Printing

1. Best choice for making silicone printing pad 
2. Different hardness
3. Good printing effects
4. Excellent quality and good resilience

Instructions for RTV-2 Silicone Rubber for Pad Printing
Preparation
Prepare the silicone pad mold, clean the pad mold with detergent, dry it with air gun, then brush a layer of release agent, and dry it again.

Mixing
Please weigh 9 gram of part A base and 1 gram of part B curing agent part B in a clean container. Thoroughly stir part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing part A and part B evenly until the part B is completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35ºC(95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent.

It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Pouring the mixture and curing
Pour the mixed Part A base silicone and part B as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours, we advice you de-mold after 24 hours, it is will improve the printing times of silicone pad.

Storage of RTV-2 Silicone Rubber for Pad Printing
When stored at or below 25 C (85F) in the original unopened containers, Silicone Base and part B Curing agent have a usable life of 12 months from the date of production. After 12 months stock, please use the Stir to mixing the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.

Packing of RTV-2 Silicone Rubber for Pad Printing
Part A base silicone: 20kg/drum or 200kg/drum
Part B Curing Agent: 1kg/bottle

Item No.	Viscosity cps	Hardness Shore A	Tear strength (KN/m)	Tensile Strength (Mpa)	Elongation break (%)	Pot life minutes	Curing Time	Linear Shrinkage
MCSIL-P30	10000 ±2000	30A ±2	30	7	580%	35min	24 hrs	≤0.1%