Liquid RTV2 Silicone for Shoe Sole Mold Making (RTV3010)

Material: Silicone Rubber
Appearance: Liquid
Item: RTV 3010
Color: White
Mixing Ratio: 100:2 / 100:3 / 100:4 / 100:5
Mixed Viscosity: 10000-11000 Cps ( Adjustable )
Samples:
US$ 0.1/kg 1 kg(Min.Order)
| Request Sample
Customization:

Contact Supplier

Gold Member Since 2013

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
RTV3010
Working Time
5-10 Mins
Curing Time
4-6 Hours
Hardness
10-13 Shore a
Tear Strength
18 N/Mm
Shrinkage
0.3%
Density(g/cm3,25 Centigrade)
1.0-1.1
Transport Package
20kg/Drum, 25kg/Drum or 200kg/Drum
Specification
REACH
Trademark
MC SILICONE
Origin
China
HS Code
39100000
Production Capacity
8000kg/Day

Product Description

Features of Shoe soles mold making:

Shoes mould Making RTV-2 Silicone Rubber is a two-component material, and RTV-2 silicone rubber is consisted of Part A silicone base and Part B CA30 curing agent, and the silicone base and curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone mould: Shoe mould making, sand casting etc.

Characteristics of Shoe soles mold making

1. Good flow ability and long working time

2. Medium hardness stone mold making

3. High tear and tensile strength

4. Easy de-mould from complex replica parts

5. Acid and alkali-resistance

6. Low linear shrinkage

Instructions for Shoe soles mold making

1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.

Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Storage of Shoe soles mold making

When the Shoes Mold Making RTV-2 Silicone Rubber is stored at or below 30 ° C (85° F) in the original unopened containers, RTV3010/3015 silicone base and CA30 curing agent have a usable life of 12 months from the date of production.

Note of Shoe soles mold making

Shoes Mold Making RTV-2 Silicone Rubber is an industrial product and must not be used in food molding, dental human skin molding applications.
 Technical parameter of shoe mold making silicone rubber
 
Item  RTV3010
Color Liquid white
Curing agent CA30
Mixing ratio 100:2
Mixed viscosity 10000 ~11000 cps
Working time 5-10 Minutes
Curing time 4-6 Hours
Hardness 10-13 Shore A
Tear Strength 18 N/mm
Tensile Strength 2.8 MPA
Relative density 1.0-1.1 g/cm3
Elongation at break 550%


 