Liquid Silicone Rubber for Plaster Moulding/RTV-2 Silicone Rubber

• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Appearance: Viscous Liquid
• Form: Liquid Rubber
• Color: White
• Mix Ratio: 2% Curing Agent
• Model NO.: MCSIL-2030
• Viscosity: 25000 Cps
• Pot Life: 30-40 Mins
• Curing Time: 4-6 Hours
• Hardness: 30 Shore a
• Tensile Strength: 3.8MPa
• Tear Strength: 30n/mm
• Shelf Life: 12 Months
• MOQ: 100kg
• Transport Package: 25kg 200kg
• Specification: RoHS, REACH, SGS
• Trademark: MC Silicone
• Origin: Dongguan
• HS Code: 39100000
• Production Capacity: 4000kg Per Day

Product Description

Product Description

RTV-2 Silicone is a two-component material, and the silicone rubber includes Part A base silicone and Part B CA30 curing agent. The Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction.

APPLICATIONS of Liquid Silicone Rubber
RTV-2 Silicone are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.

FEATURES of Liquid Silicone Rubber
1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage (0.3%)

Product Parameters

How to make the silicone mold?
The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
Mixing
Please weight 100 Part A base and 2 parts of Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent. It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Pouring the mixture and curing
Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Item no.	MCSIL-2030
Color	white
Viscosity	25000 cps
Mix ratio	100:2
Pot life	30-40 mins
Curing time	4-6 hrs
Hardness	30 shore A
Tensile strength	3.8 Mpa
Elongation	480%
Tear Strength	30 N/mm
Shrinkage	0.3%

 

Packaging & Shipping

PACKAGE of Liquid Silicone Rubber

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle, 1kg/bottle

STORAGE of Liquid Silicone Rubber

RTV-2 Silicone Rubber which is an environmentally-friendly liquid silicone product, is not easy to burn and can be stored and transported as non-hazardous goods. The shelf life of the product is about one year from the date of production. Inspection is required when exceeding the time limited. It can continue to be used in case of neither thickening nor deterioration.