RTV-2 Silicone Component for Grc Decor Mouldings

Raw Material: Silicone Rubber Raw Material
Material: Silicone Rubber
Appearance: Liquid White
Form: Liquid Rubber
Color: White
Hardness: 25 Shore a
Customization:
Gold Member Since 2013

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
MCSIL-2025 SILICONE
Viscosity
25000 Cps
Curing Agent
Tin Catalyst
Mix Ratio
2%
Pot Life
30-40 Mins
Curing Time
4-6 Hrs
Tensile Strength
3.8 Mpa
Transport Package
25kg, 200kg
Specification
MSDS, REACH, SGS
Trademark
MC Silicone
Origin
Dongguan
HS Code
3910000000
Production Capacity
4000kg Per Day

Product Description

Description of RTV-2 Silicone for GRC Decor Mouldings

RTV-2 Silicone is a two-component material, and the silicone rubber includes Part A base silicone and Part B CA30 curing agent. The Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These silicone materials can be cast into the cured silicone mold: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...

Features of RTV-2 Silicone for GRC Decor Mouldings

1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage

Applications of RTV-2 Silicone for GRC Decor Mouldings

RTV-2 Silicone are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.

How to make the silicone mold?

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35° C (95° F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.

Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Storage of RTV-2 silicone

When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.

Need more information, please feel free to contact Nicole.
 Item no. MCSIL-2025
 Color  white
 Hardness  25 shore A
 Tensile strength  3.8 Mpa
 Elongation  500%
 Tear Strength  30 N/mm
 Shrinkage  0.3%