| Raw Material: | Synthetic Rubber |
|---|---|
| Material: | Silicone Rubber |
| Appearance: | Liquid |
| Form: | Liquid Rubber |
| Item: | Mcsil-2030 |
| Color: | off-White Liquid Silicone Rubber |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Description of white Tin Cure RTV-2 Silicone Liquid Rubber
RTV2 silicone rubber is a kind of two-component material, that is the mold making silicone rubber made up of Part A base silicone and Part B curing agent. The mixed Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction,then become a silicone rubber mold that can be used for objects reproduction.
Features of white Tin Cure RTV-2 Silicone Liquid Rubber
The formed mold can be used repeatedly without deformation and water shrinkage and with high temperature resistance, thereby providing high duplication times, with Low shrinkage(0.3%)Applications of white Tin Cure RTV-2 Silicone Liquid Rubber
RTV-2 Liquid Silicone Rubber MCSIL-2030 is good for casting Plasters, Cements and resin, toy craftworks, gifts and stationery, large statues, duplication of cultural relics mold making, etc.
How to make the silicone mold?
The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
l Mixing
Please weight 100 Part A base and 2 parts of Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent. It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
l Pouring the mixture and curing
Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.
20kg/drum, 25kg/drum or 200kg/drum of silicone rubber Part A
0.8kg/bottle, 1kg/bottle of silicone rubber Part B