Gold Member Since 2013
Mingcheng Group Limited

Silicone Rubber, Silicone, Gypsum Mold Making Silicone manufacturer / supplier in China, offering Gypsum Mold Making Silicone Rubber (MCSIL-H25), Liquid Silicone Rubber for Silicon Moulds for Candles, RTV-2 Liquid Silicone for Casting Molds (RTV930) and so on.

(/ )

Supplier Homepage Product Gypsum, Plaster Decoration Products Molding Gypsum Mold Making Silicone Rubber (MCSIL-H25)

Gypsum Mold Making Silicone Rubber (MCSIL-H25)

FOB Price: US $5.8 / kg
Min. Order: 200 kg
Min. Order FOB Price
200 kg US $5.8/ kg
Get Latest Price
Production Capacity: 4000kg/Day
Transport Package: 20kg/Drum, 25kg/Drum or 200kg/Drum
Payment Terms: L/C, T/T, Western Union, Paypal

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: MCSIL-H25 silicone rubber
  • Material: Silicone Rubber
  • Form: Liquid Rubber
  • Color: off-White
  • Hardness: 27-28 Shore a
  • Elongation at Break: 511%
  • Specification: REACH, MSDS, SGS
  • HS Code: 39100000
  • Raw Material: Silicone Rubber Raw Material
  • Appearance: Liquid
  • Item: Mcsil-H25
  • Mixing Ratio: 100:2
  • Tear Strength: 30n/Mm
  • Trademark: MC SILICONE
  • Origin: Dongguan, China
Product Description
Description of Gypsum Mold Making Silicone Rubber

Gypsum Mold Making Silicone Rubber is a two-component material, this kind of silicone rubber consists of Part A base silicone and Part B CA30 curing agent, and Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone molds: Plaster polyurethane, PU, GRC, cement, resin, polyester, wax etc...

Features of Gypsum Mold Making Silicone Rubber

1. Good flowability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage

Applications of Gypsum Mold Making Silicone Rubber

MCSIL-H25 silicone rubber is suitablr for gypsum mold making.

How to make the silicone mold?

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Packing of Gypsum Mold Making Silicone Rubber

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle

Storage of Gypsum Mold Making Silicone Rubber

When the RTV-2 silicone rubber is stored at or below 30 C (85F) in the original unopened containers, Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production.

Note of Gypsum Mold Making Silicone Rubber

RTV2 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.

Need more information, please feel free to contact Nicole.
ItemMCSIL-H25
Coloroff-white
Curing agentCA30
Mixing ratio100:2
Hardness27-28 Shore A
Tear Strength30 N/mm
Tensile Strength4.5 Mpa
Shrinkage≤0.3%
Send your message to this supplier
Avatar
Miss Libby Deng
*From:
To: Miss Libby Deng
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category