RTV184 Two Parts Transparent Electronic Potting Silicone Compound Clear Silicone Encapsulant

• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Appearance: Liquid Silicone Rubber
• Form: Liquid Rubber
• Application: LED PCB Silicone Potting Compound
• Mixing Ratio: 10:1
• Model NO.: MCSIL-E184
• Mixed Viscosity: 3000~4000cps
• Pot Life: 1.5~2.5 Hrs
• Curing Time: 24 Hrs
• Hardness: 42 Shore a
• Shelf Life: 12 Months
• Transport Package: Can/Plastic Drum
• Specification: 20kg/drum
• Trademark: MC silicone
• Origin: China
• HS Code: 3910000000
• Production Capacity: 4000kg Per Day

Product Description

      RTV184 Two Parts Transparent Electronic Potting Silicone Compound Clear Silicone Encapsulant

Description
Silicone MCSIL-E184 is supplied as a two-component 10 to 1 liquid silicone addition cure system. It consists of Part A and Part B. When two components are thoroughly mixed, the mixture cures to a flexible elastomer, which is well suited for the protection of electrical/electronic applications.

Features
Good Flow ability
Room temperature and heat cure
Good dielectric properties
Rapid, versatile cure processing controlled by temperature
High transparency allows easy inspection of components

Typical properties

Item No.	MCSIL-E184
Appearance	Transparent
Viscosity	3000~4000
Mix ratio	10:1
Working Time	90 mins
Curing time	24-48 hours
Hardness	42 shore A
Heat Cure Time at 100ºC	30-40 minutes
Heat Cure Time at 150ºC	10 minutes
Thermal conductivity	0.27
Volume resistivity	2.9E+14 ohm*cm
Dielectric Strength	19 kV/mm
Tensile strength	6.7 Mpa
Dielectric Constant at 100 kHz	2.68

Applications
excellent electrical property features in resistant to temperature, corrosion, radiation, insulation, waterproof, damp proofing, shock resistance, thermal conducting, inflaming retarding and weather ability, etc. Adhesive and coating for solar power, HID, LCD displayers, circuit board and electronic components, etc.


Using Instruction
1.Preparing Surfaces
In applications requiring adhesion, priming will be required for many of the silicone encapsulants. For best results, the primer should be applied in a very thin, uniform coating and then wiped off after application. After application, it should be thoroughly cured prior to application of the silicone elastomer.
2.Processing & Curing
MC Silicone E184 part A and Part B should be thoroughly mixed at a 10:1 ratio , may be poured/dispensed directly into the container in which it is to be cured. Care should be taken to minimize air entrapment. When practical, pouring/dispensing should be done under vacuum, particularly if the component being potted or encapsulated has many small voids. If this technique cannot be used, the unit should be evacuated after the silicone encapsulant has been poured/dispensed. MC silicone encapsulants may be either room temperature (25°C/77°F) or heat cured. Room temperature cure encapsulants may also be heat accelerated for faster cure. Ideal cure conditions for each product are given in the product selection table.
3.Pot life and curing rate
Cure reaction begins with the mixing process. Initially, cure is evidenced by a gradual increase in viscosity, followed by gelation and conversion to a solid elastomer. Pot life is defined as the time required for viscosity to double after base and curing agent are mixed and is highly temperature and application dependent. Please refer to the data table.
4.Useful Temperature Ranges
For most uses, silicone elastomers should be operational over a temperature range of -45 to 200°C (-49 to 392°F) for long periods of time. However, at both the low and high temperature ends of the spectrum, behavior of the materials and performance in particular applications can become more complex and require additional considerations and should be adequately tested for the particular end-use environment.

Packing and Storage

1. Silicone rubber is shipped as kits that Part A and B liquid components in separate containers. It is available in packing in 5kg or 20kg,200kg per pail.
2. Silicone rubber must be tightly sealed in cool and dry place, prevented from sun and rain. Transport by non-dangerous goods.