| Material: | Silicone Rubber |
|---|---|
| Appearance: | Viscous Liquid |
| Color: | White |
| Hardness: | 24 Shore a |
| Viscosity: | 20000 Cps |
| Mix Ratio: | 100:5 |
| Customization: |
|---|
Suppliers with verified business licenses
DESCRIPATION
Silicone rubber MCSIL-H20 is a two-component material, consisting of Part A base and Part B MCSIL-CA30, cures at room temperature by a condensation reaction. It is super silicone liquid rubber material for polyurethane resin molds making.
PRODUCT FEATURES
1. Good flow ability and long working time
2. High duplication times
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
Technical Data
| Item No. | MCSIL-H20 |
| Color | Translucent |
| Curing Agent | CA-45 |
| Mixing ratio | 100:2 |
| Mixed Viscosity | 20000cps |
| Working time | 45mins |
| Curing time | 6 hours |
| Hardness | 20±2 shore A |
| Tear Strength | 32 N/mm |
| Tensile Strength | 4.2Mpa |
| Shrinkage | ≤0.3% |
| Elongation | 550% |
USING INSTRUCTION
1- Take 100g of part A and add 2g of part B and mix the silicone rubber and curing agent evenly.
2- vacuum pumping
Without exception, this step takes less than 10 minutes. Otherwise, it will cause , and no more further steps will be available
3- Pouring mold or block mold of silicone rubber
The pouring way is an easy way to make molds, it's slowly and evenly pour into the mixed silicon rubber into the square frame. After the cross linking reaction.
APPLICATIONS
RTV-2 silicones are specifically designed to replicate stones, marble, wood, and other construction materials, producing outstanding fidelity for every detail, including veins and surface texture. The various grades of architectural molding silicones enable builders to replicate accurately the look they desire while providing long mold life and excellent resistance against casting materials.
Package
Part A base silicone: 5kg, 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 250g, 800g/bottle, 1kg/bottle
Certificates
Storage
When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, Silicone Base and Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
Benefits of MC Silicone
Ease of processing
High resin resistance increasing the number of cast parts
Low linear shrinkage for greater accuracy
Easy release of shapes, including large pieces and complex geometries
High compatibility with water-rich casting materials such as gypsum
Increased compatibility with high performance concrete
Dimensional stability due to very low shrinkage
High mechanical properties over a range of flexibility
| Item no. | RTV 2024 |
| Color | white |
| Viscosity | 20000±2000 cps |
| Mix ratio | 100:5 |
| Pot life | 90-120 mins |
| Curing time | 18-24 hrs |
| Hardness | 21-24 shore A |
| Tensile strength | 4.7 Mpa |
| Elongation | 544% |
| Tear Strength | 34 N/mm |
| Shrinkage | 0.3% |