Resin Mold Making Silicone Rubber

• Customization: Available
• Raw Material: Silicone Rubber Raw Material
• Material: Silicone Rubber
• Model NO.: MCSIL-2015 silicone rubber
• Form: Liquid Rubber
• Item: Mcsil-2015
• Color: off-White
• Mixing Ratio: 100:2
• Hardness: 13-15 Shore a
• Tear Strength: 25 N/Mm
• Tensile Strength: 3.8 MPa
• Elongation at Break: 600%
• Transport Package: 20kg/Drum, 25kg/Drum or 200kg/Drum
• Specification: REACH, MSDS, SGS
• Trademark: MC SILICONE
• Origin: Dongguan, China
• HS Code: 39100000
• Production Capacity: 4000kg/Day

Product Description

Description of Resin Mold Making Silicone Rubber

RTV-2 silicone rubber is a two-component material, which consists of Part A base silicone and Part B CA30 curing agent; Then the silicone base and curing agent can cure at room temperature by a condensation reaction. These silicone rubber materials can be cast into the cured silicone mold: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc.

Specifications of RTV-2 Silicone Rubber

1. Good flow ability and long working time
2. Low hardness, easy de-mold
3. High tear and tensile strength
4. Acid and alkali-resistance
5. Low linear shrinkage

Applications of RTV-2 Silicone Rubber

RTV-2 silicone rubber can be applied in many objects mold making, since the RTV-2 silicone has good flow ability and medium hardness, and the silicone can cure at room temperature, thus it's a good material for duplication.

RTV-2 Silicone Rubber can be used for artificial stone moldmaking.For example MCSIL-2066 and MCSIL-2088 silicone.
 
RTV-2 silicone rubber can be appliied in candle and soap moldmaking, such as MCSIL-215 and MCSIL-218 silicone.
 
RTV-2 silicone rubber can be used for plaster moldmaking, such as MCSIL-2025,MCSIL-H25 and MCSIL-2030 silicone.
 
RTV-2 silicone rubber can be applied in the field of shoe sole moldmaking, for example, MCSIL-S10 and MCSIL-S15 silicone.
 
RTV-2 silicone rubber can be used for prototyping and electronic potting.

How to make the silicone mold?

1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.

Storage of RTV-2 Silicone Rubber

When the silicone rubber is stored at or below 30C (85F) in the original unopened containers, RTV2 silicone base and curing agent have a usable life of 12 months from the date of production.

Note of RTV-2 Silicone Rubber

RTV2 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.

Packing of RTV-2 Silicone Rubber

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle

Need more information, please feel free to contact us.

Item	MCSIL-2015
Color	off-white
Curing agent	CA30
Mixing ratio	100:2
Hardness	13-15 Shore A
Tear Strength	25 N/mm
Tensile Strength	≥3.8 Mpa
Shrinkage	≤0.3%
Elongation at break	600%
Relative density	1.1-1.15 g/cm3