DESCRIPTION
Two Components Mold Making Silicone Rubber is generally named as two-part silicone rubbers which vulcanise, or cure, at room temperature. Part A is a dynamic liquid silicone/Part B is the curing agent (tin catalyst).
APPLICATIONS
Two Components Mold Making Silicone Rubber can be used for construction of moulds for gypsum, soap, candles, concrete, resin products, artificial (very lightweight) stone, wax or custom moulds;
Two Components Mold Making Silicone Rubber can be used for making decorative building moulds (cornice, column, balustrade, ceilling roses, pedestals, fountains, mantels, wall ornament, planter etc;
ADVANTAGES
Exceptional fluidity and good operability, easy to demold.
Cures at room temperature within 3-4 hours (assuming constant temp of 25 degrees C).
Good tensile and tear strength, low shrinkage (<0.3%)
High duplication levels or longevity
Good resistance to weather, temperature, aging, acid.
Long shelf life (12 months at least) if kept at constant temperatures.
STORAGE
Two Components Mold Making Silicone Rubber is an environmentally-friendly liquid silicone product, is not easy to burn and can be stored and transported as non-hazardous goods. The shelf life of the product is about 12 months from the date of production. Inspection is required when exceeding the time limited. It can continue to be used in case of neither thickening nor deterioration.
PACKAGE
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle, 1kg/bottle
COMPANY INFORMATION
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series, we are competitive in price with good quality.
Should you have any question, please feel free to contact us.
MINGCHENG GROUP LIMITED
| Item no. |
MCSIL-H20 |
| Color |
white |
| Viscosity |
25000±2000 cps |
| Mix ratio |
100:2 |
| Pot life |
30-40 mins |
| Curing time |
4-6 hrs |
| Hardness |
20 shore A |
| Tensile strength |
3.8 Mpa |
| Elongation |
600% |
| Tear Strength |
30 N/mm |
| Shrinkage |
0.3% |