High Transparent Mould Making Platinum RTV2 Clear Liquid Silicone Rubber

• Customization: Available
• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Model NO.: MCPLA-H40 Silicone rubber
• Appearance: Liquid
• Form: Liquid Rubber
• Item: Mcpla-H40
• Color: Clear Transparent
• Mixing Ratio: 10:1
• Viscosity: 45000~50000cps
• Pot Life: 60~90min
• Curing Time: 24hrs
• Hardness: 40 Shore a
• Tensile Strength: 6 MPa
• Tear Strength: 27 N/mm
• Shelf Life: 12 Months
• Transport Package: 20kg/Drum or 200kg/Drum
• Specification: REACH, MSDS, SGS
• Trademark: MC SILICONE
• Origin: Dongguan, China
• HS Code: 39100000
• Production Capacity: 4000kg/Day

Product Description

             High Transparent mould making platinum RTV2 clear liquid silicone rubber

Description of RTV T4 Silicone Rubber
MCPLA-H series silicone rubber is two-component addition type silicone rubber , liquid silicone rubber is a two component elastomer cross-linking at room temperature. The polymerization can be accelerated by heat. The silicone components are delivered as liquids, which once mixed and cured transform into a transparent, elastic and resistant material. Polymerization occurs without formation of heat.
 

Properties	MCPLA-H40 A	MCPLA-H40B
Appearance	Viscous liquid	Liquid
Color	Transparent	Clear
Viscosity(at 23°C,mPa.s,approx.)	55000	4000
Specific Gravity(g/cm3,approx.)	1.08	1.08
Proportion(A:B)	100	10
Mixing viscosity(at 23°Capprox.)	55000
Max working time(at 23°C,minutes)	60
Demoulding time(at 23°C,hrs,approx.)	24
Hardness Shore A(after 24 h)	40
Tensile Strength(Mpa,after 24 h)	5-6
Elongation(%)	400
Tear Strength(N/mm)	25

Features:
Outstanding release properties
Cure can be heat accelerated
High transparent appearance to cut split lines
Very low shrinkage and good dimensional stability
High hardness, but flexible and very tough
Can be used for high temperature casting applications

Applications:
Two-component addition type silicone rubber can be used for Label manufacturing, Molding applications requiring low shrinkage e.g. toys, jewelry, automotive, rapid prototyping etc.



INSTRUCTION:Processing and Instructions of Addition Cure Silicone
1. Mixing the two components
According the mixing ration 10:1 weighting A and B, the two components may be thoroughly mixed either by hand or using a low-speed electric to minimize the degassing of bubbles and to avoid any temperature increase.
Note: It is also possible to use a special mixing and dispensing machine for the silicone components, further information is available upon request.
2. Moulding
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3-4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter/height ratio (3 to 4 times of the initial volume)
3. Polymerisation
The curing may be slowed down at lower temperature or accelerated by applying heat.
Note:
1.Contamination from sulfur (e.g., sulfur-based clay), amines, tin compounds, cured polyester resin, some paints and some silicone rubbers may inhibit surface cure of platinum-cured rubbers.
 2.Apply a release agent, Although not usually necessary, a release agent will make demolding easier when casting into most surfaces.

Storage and shelf life
When the silicone rubber is stored at or below 25 degree Celsius in the original unopened containers, Silicone Base and Curing agent have a usable life of 12 months from the date of production. After 12 months' stockpiles, please use tool to stir the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
1.Store the original packing tightly sealed and at a temperature below 25 degree Celsius.
Use the product as soon as the packaging has been opened.
2.Close the lid tightly after taking out the proper amount of liquid silicone rubber.

Package:
20kg per drum, 200kg per drum
20kg/drum;480kg/pallet or 640kg/pallet.