Cheap RTV2 Liquid Tin Cure Silicone Rubber for Concrete Molds Making

Product Description

Cheap RTV2 liquid silicone rubber for concrete,sand molds making tin cure silicone mold rubber
 

Item No.	Properties before curing							Curing
	Part A	Part B		Part A+ Part B				Pot life at 25^0C		De-molding Time at 25ºC
	Appearance	Appearance		Ratio		Viscosity
MCSIL-3028	White	Clear		100:2		25000±2000 cps		30-40 mins		4-6 hours
	Properties after curing 24 hours
	Hardness Shore A		Tear strength		Tensile Strength		Elongation break (%)		Linear Shrinkage
	28		25N/mm		3.0 Mpa		450-500		0.2-0.4%

Description of RTV-2 Silicone Rubber
RTV-2 silicone rubber is a two-component material, the silicone consists of Part A silicone base and Part B CA30 curing agent, and the silicone base and curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone mold: Shoe mold making, sand casting etc.

Specifications of RTV-2 Silicone Rubber
1. Good flow ability and long working time
2. Medium hardness
3. Easy de-mould from shoe mold
4. Low linear shrinkage

Applications of RTV-2 Silicone Rubber
MCSIL-S silicone rubber is suited for shoe mold, simple products, sand casting mold making, and shoe mold by pouring way.


How to make the silicone mold?

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Storage of RTV-2 Silicone Rubber

When the silicone rubber is stored at or below 30 C (85F) in the original unopened containers, silicone base and CA30 curing agent have a usable life of 12 months from the date of production.

Packing of RTV-2 Silicone Rubber
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle