Easy Mold Two Parts Resin Silicone Mold Putty Silicon Impression Putty

• Customization: Available
• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Model NO.: MC-SP35
• Form: Liquid Rubber
• Item No.: Mc-Sp35
• Mix Ratio: 1:1
• Pot Life (Mins): 3-5mins
• Curing Time (Hrs): 20-30mins
• Hardness (Shore a): 35 Shore a
• Tensile Strength(MPa): 2.5
• Elongation Break: 350%
• Shrinkage: 0.1%
• Shelf Life: 12 Months
• Transport Package: Can
• Specification: 350g 500g 1kg, 5kg, 10kg, 25kg
• Trademark: MC silicone
• Origin: China, Guangdong
• HS Code: 39100000
• Production Capacity: 400kg/Day

Product Description

 

MC- Silicone PUTTY is a hydrophilic addition silicone rubber impression material, it contains two components, Part A is platinum catalyst, and Part B is hydrogen containing polysiloxane. This product comprises liquid material and powder material. The main raw material is a silicone oil, silicone resin, alumina, quartz powder and etc.
MC- Silicone PUTTY are new silicone compounds (platinum catalyst) that can be easily mixed and applied by hand to a variety of surfaces. Silicone Putty is mixed in equal amounts (1A:1B) by volume/weight.MC-P35 has a pot life of about 5-20minute with a cure time of about 30-60 min at room temperature (73°F/23°C). Shrinkage is low and cured rubber is exceptionally strong (very high tensile strength), durable and will resist high temperatures (for casting low-temperature melt metal alloys). They also resist cure inhibition.MC-P35 are also SKIN SAFE and can be used for culinary applications.

 

Features of Silicon Impression Putty:
-Easy to use, 3 Minute working time, 25 minute cure.
-Ideal for small molds, excellent detail from original.
-Strong, flexible, reusable molds.
-High Heat range, up to 400°F.
-No Shrinkage.
-Self releasing, no mold release agent required for most applications.
-Odorless, Non Toxic. Skin safe.

Application of Silicon Impression Putty:
Applications include making fast mold impressions from almost any surface, miniatures, toys, chocolate & candy, orthotics / orthopedic, equine hoof repair, jewelry mold making, resin crafts, etc.
 

Physical Properties:

Before Curing	Catalyst Components	Base Components
Appearance	White putty	Blue putty
Mix ratio	1:1
Pot life	3-5 minutes
Curing time(37C)	<30 minutes
After Curing
Hardness(Shore A)	35
Permanent deformation %	<0.2%
Dimensional stability %	<0.25
Copy details(μm)	<1.5
tensile Strength Mpa	2.5
Temperature stability	60°C for 1 week
Elongation%	350

Usage Instruction

 

1. Under the room temperature, take the same amount of base component (blue) and catalyst component (white).

 

2. Mix the two components together. It is recommended to use the blue spoon to take the base component and white spoon to take catalyst  component.

 

3. Use your fingertips to mix the two components together and knead for at least 30 seconds until they are mixed completely.

 

4. Close the lid immediately after usage, the cover can not be interchanged.

 

Package of Silicon Impression Putty:

Package available in 350g, 500g, 1kg,5kg,10kg, 25kg. sampe available in 100gA+100gB.





 

Storage of Silicon Impression Putty:

it has a shelf life of 12 month in original package at a cool dry place.

 

Precautions

1. Do not use natural rubber gloves. It is recommended to use disposable polyethylene plastic gloves.

2. The product contains platinum catalyst, sulfur, phosphorus, amine, etc. will slow down or even stop the curing reaction, and thus it must avoid sulfur, phosphorus, amine, acrylic and meth acrylic acid esters and other chemical products in use.

3. Close the lid tightly and immediately after use, keep it in cool place, and be refrigerated in summer.

4. The temperature has a significant impact on the curing time; the curing reaction will slow down at low temperature, and speed up at high temperature curing speed. It should adjust operation rhythm according to the environment and the finger temperature.

5. It is strictly recommended to use the same amount of base and catalyst. Unequal amount will lead to delayed or accelerated cure.

 

MAKE YOUR OWN MOLDS THE EASY WAY - Simply knead equal parts of A and B together to form strong, flexible, reusable molds with excellent details. No liquids to mix together, no release agents required, no mold boxes or other equipment required.

MAKE YOUR OWN REUSABLE MOLDS THE FAST WAY - You have up to 15 minutes working time and you can de-mold in only 1-2 hours. High heat range up to 450 F.

TONS OF USES - Ideal for small molds for small impression molding, soap molds, candle molds, jewelry making and repair, antique furniture repair and other small object casting.

CAST MANY TYPES OF MATERIALS - Moldable plastics, waxes, clays, urethane and epoxy resins, plaster and even some low melt metals.

NON-TOXIC & ODOR FREE