Shoe Sole Mold Making RTV2 Silicone Rubber Material

Raw Material: Silicone Rubber Raw Material
Material: Silicone Rubber
Appearance: Liquid
Form: Liquid Rubber
Item: Mcsil-S20
Color: off-White
Customization:

Contact Supplier

Gold Member Since 2013

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
MCSIL-S Silicone Rubber
Mixing Ratio
100:2
Mixed Viscosity
12000-13000 Cps
Hardness
18-20 Shore a
Tear Strength
20 N/Mm
Transport Package
20kg/Drum, 25kg/Drum or 200kg/Drum
Specification
REACH, MSDS, SGS
Trademark
MC SILICONE
Origin
Dongguan, China
HS Code
39100000
Production Capacity
4000kg/Day

Product Description

Description of Shoe Sole Mold Making RTV2 Silicone Rubber

Shoe Sole Mold Making RTV2 Silicone Rubber is a two-component material, the silicone consists of Part A silicone base and Part B CA30 curing agent, and the silicone base and curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone mold: Shoe mold making, sand casting etc.

Specifications of Shoe Sole Mold Making RTV2 Silicone Rubber

1. Good flow ability and long working time
2. Medium hardness
3. Easy de-mould from shoe mold
4. Low linear shrinkage

Applications of Shoe Sole Mold Making RTV2 Silicone Rubber

MCSIL-S20 silicone rubber is suited for shoe mold, simple products, sand casting mold making, and shoe mold by pouring way.


How to make the silicone mold?

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Storage of Shoe Sole Mold Making RTV2 Silicone Rubber

When the silicone rubber is stored at or below 30 C (85F) in the original unopened containers, RTV silicone base and CA30 curing agent have a usable life of 12 months from the date of production.

Note of Shoe Sole Mold Making RTV2 Silicone Rubber

RTV silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.

Packing of Shoe Sole Mold Making RTV2 Silicone Rubber

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle

Need more information, please feel free to contact Nicole.
Item No.MCSIL-S20
Coloroff-white
Curing agentCA30
Mixing ratio100:2
Mixed viscosity12000-13000 cps
Hardness18-20 Shore A
Tear Strength20 N/mm