Transparent Addition Cure RTV2 Liquid Silicone Rubber for Ear Plug

• Customization: Available
• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Model NO.: MCPLA-H30 Silicone rubber
• Appearance: Liquid
• Form: Liquid Rubber
• Item: Mcpla-H30
• Color: Transparent
• Mixing Ratio: 100:10
• Mixed Viscosity: 40000cps
• Working Time: 90~120 Mins
• Curing Time: 24hours
• Hardness: 30 Shore a
• Tensile Strength: 6.2 MPa
• Tear Strength: 28n/mm
• Elongation at Break: 350%
• Shrinkage: 0.1%
• Shelf Life: 12 Months
• Transport Package: 20kg/Drum
• Specification: REACH, MSDS, SGS
• Trademark: MC SILICONE
• Origin: Dongguan, China
• HS Code: 39100000
• Production Capacity: 4000kg/Day

Product Description

Transparent Addition Cure RTV2 Liquid Silicone Rubber for Ear Plug

Description of Transparent Addtion Cure RTV2 Silicone Rubber

RTV silicone rubber is a two component elastomeric cross-linking at room temperature. The polymerization can be accelerated by heat (max. 150 C). The silicone components are delivered as liquids, which once mixed and cured transform into a transparent, elastic and resistant material. Polymerization occurs without formation of heat.

Advantages of Transparent Addtion Cure RTV2 Silicone Rubber

1. Easy Curing: MCPLA-H40 polymerizes at room temperature (23C).
2. High Transparency
3. High tear and tensile strength
4. Long shelf life with low shrinkage

Applications of Transparent Addtion Cure RTV2 Silicone Rubber

Label manufacturing, Molding applications requiring low shrinkage, such as toys, jewelers, automotive, rapid prototyping etc.


Instructions for making silicone molds

1. Mixing the two components
According the mixing ratio 10: 1 weighting part A and B, the two components may be thoroughly mixed either by hand or using a low speed electric to minimize the entrance of air and to avoid any temperature increase.
Note: It is also possible to use a special mixing and dispensing machine for the two silicone components, further information is available upon request.

2. Molding
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter/height ratio(3 to 4 times of the initial volume)

3. Polymerization
The curing may be slowed down at lower temperature or accelerated by applying heat.
Note: In general contact with certain materials can inhibit the cross linking of RTV.
Natural rubbers vulcanized with sulfur
RTV elastomeric is catalyzed with metal salts, e. G. Tin compounds
PVC stabilized with tin salts and additives
Epoxy catalyzed with amines
Certain organic solvents, such as Ketones, alcohols, ether etc.

In case of doubt, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.

Storage and shelf life of Transparent Addtion Cure RTV2 Silicone Rubber

Silicone RTV must be used within 12 months from the manufacturing date. Beyond this date, MC silicone no longer guarantees the products confirms with the sales specification. 


Packaging of Transparent Addtion Cure RTV2 Silicone Rubber

Part A: 20kg/drum; Part B: 2 kg /drum
Special containers are available are on request.