General decription of Plaster Molding Silicone Liquid Rubber
RTV-2 Silicone Rubber for Molding is generally named as two-part room temperature cure silicone rubber, RTV-2 Silicone Rubber features an exceptional fluidity and good operability. When mixed with 2% curing agent, they can still be operated within 30 minutes, but will be formed after 4-6 hours. RTV2 Silicone Rubber features with resistance to deformation, high temperature, acid and alkali, and expansion. RTV2 Silicone Rubber flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle mold, etc.
Features of Plaster Molding Silicone Liquid Rubber
1-RTV-2 silicone rubber for molding has an exceptional fluidity and good operability.Applications of Plaster Molding Silicone Liquid Rubber
MCSIL-20 series RTV2 silicone rubber also can be applied in the reproduction of cement molding, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. Etc.
Package of Plaster Molding Silicone Liquid Rubber
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
How to make the silicone mold?
The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
l Mixing
Please weight 100 Part A base and 2 parts of Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent. It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
l Pouring the mixture and curing
Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.
Storage of white Tin Cure RTV-2 Silicone Liquid Rubber :
When stored at or below 30 C (85F) in the original unopened containers, silicone base and CA30 Curing agent have a usable life of 12months from the date of production. After 12 months stock, please use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again, no influence for other performances.
Professional factory of RTV-2 Molding Silicone: