Product Description:
MC-EP2009A/B is a two-component transparent epoxy resin adhesive that cures at room temperature. It has the following characteristics: low mixing viscosity, good de-aeration; long working time at room temperature, rapid curing at medium temperature; excellent mechanical properties after curing, low shrinkage ; The cured product has good light transmittance and other advantages.
Applications:
It is mainly used for forming river tabletops, countertop, coffee table and large transparent crafts.
Using Instruction:
1. Weighing: Weigh the materials A and B according to the weight ratio (3:1)
2. Mixing: Mix the weighed A and B materials and stir evenly.
3. Pouring: Pouring the mixed A and B materials into the objects to be poured, and curing at room temperature (complete curing in 24 hours).
Mixing ratio (A:B) 3:1
Working time 25ºC: 120-180 minutes
Initial curing time 25ºC: 6-8 hours
Curing conditions 25ºC: 24 hours or 70ºC in 1-2 hours
Physical Properties
|
Item No. |
MC-EP2009 A |
MC- EP2009 B |
|
Appearance |
Clear liquid |
Clear liquid |
|
Density 25ºC,g/cm3 |
1.1~1.2 |
0.9~1.1 |
|
Viscosity 25ºC,Pa.s |
800~1000 |
200~300 |
|
After Curing |
||
|
Hardness |
SHORE-D |
>85 |
|
Volume resistivity |
25ºC,Ω,CM |
4.0×1015 |
|
Surface resistivity |
25ºC,Ω |
2.5×1014 |
|
Dielectric strength |
25ºC,KV/MM |
23 |
|
Linear expansion coefficient |
CM/K |
<6.0×10-5 |
|
Water absorption |
100ºC/1H,% |
<0.4 |
|
Glass transition temperature |
ºC |
>100 |
|
Working temperature |
ºC |
-60-120 |
The above performance data is typical data measured in a laboratory environment with a temperature of 25°C and a humidity of 70%. It is for customer reference only.
Packaging:
5kg per bottle, 20kg per carton
Storage: It has a shelf life of 12 months in original package in a cool dry and ventilated place.