Ornaments Mold Making Liquid Silicone Rubber/RTV-2 Silicone

Product Details
Customization: Available
Material: Silicone Rubber
Appearance: Liquid
Manufacturer/Factory
Gold Member Since 2013

Suppliers with verified business licenses

Terms of Payment
LC, T/T, D/P, PayPal, Western Union, Small-amount payment, Money Gram
OEM/ODM Availability
Yes
Find Similar Products

Basic Info.

Model NO.
MC silicone
Form
Liquid Rubber
Item
RTV2015
Color
White
Mixing Ratio
100:2 / 100:3 / 100:4 / 100:5
Mixed Viscosity
25000-26000 Cps ( Adjustable )
Working Time
30-40 Mins
Curing Time
4-6 Hours
Hardness
13-15 Shore a
Tear Strength
25 N/mm
Elongation
511%
Density(g/cm3,25 Centigrade)
1.10-1.15
Transport Package
20kg/Drum, 25kg/Drum or 200kg/Drum
Specification
REACH, MSDS, SGS
Trademark
MC SILICONE
Origin
China
HS Code
39100000
Production Capacity
8000kg/Day

Product Description

Brief Introduction of different hardness RTV silicone rubber

RTV-2 silicone rubber is a two component material, and it consist of Part A base silicone and Part B curing agent. When the two parts mix together and pour or brush on a object, the silicone base and curing agent can cure to be a silicone mold at room temperature; And 24 hours later, the silicone mold can be released from the object, and then the silicone mold can be poured into the following material to copy: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...

Procedures of different hardness RTV silicone rubber

1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.

Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Extensive Applications of different hardness RTV silicone rubber

RTV-2 silicone rubber can be used in the duplication of cement molds, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.
 Technical parameter of RTV silicone rubber for concrete mold making
 
Item No.   RTV2028
Color     white
Curing agent    CA30
Mixing ratio     100:2
Mixed viscosity   28000-30000 cps
Working time      30-40 Minutes
Curing time   4-6  Hours
Hardness   28 Shore A
Tear Strength     30 N/mm
Tensile Strength    4.5 MPA
Shrinkage        ≤0.3%

Need more information , please feel free to contact us .
 
MINGCHENG GROUP LIMITED
Contact : Sophie
 
Tel : 0086-769-82693920 
 
 
ADD : No.2, Zhouliao Road, Langzhou Industrial Zone, Changping, Dongguan, Guangdong, China

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier