Liquid RTV-2 Silicone Rubber for Making Soap Molds

• Customization: Available
• Raw Material: Silicone Rubber Raw Material
• Material: Silicone Rubber
• Model NO.: MCSIL-215/218 Silicone rubber
• Form: Liquid Rubber
• Item: Mcsil-218
• Color: off-White
• Mixing Ratio: 100:2
• Mixed Viscosity: 22000-23000 Cps
• Working Time: 30-40 Mins
• Curing Time: 4-6 Hours
• Hardness: 18-20 Shore a
• Tear Strength: 18-20 N/Mm
• Tensile Strength: 3.8 Mpa
• Elongation at Break: 520%
• Transport Package: 20kg/Drum, 25kg/Drum or 200kg/Drum
• Specification: REACH, MSDS, SGS
• Trademark: MC SILICONE
• Origin: Dongguan, China
• HS Code: 39100000
• Production Capacity: 4000kg/Day

Product Description

Description of RTV-2 Silicone Rubber for Soap Mold Making
 
RTV-2 silicone rubber is a two-component material, which consists of Part A base silicone and Part B CA30 curing agent; then the silicone base and curing agent can cure at room temperature by a condensation reaction. These silicone rubber materials can be cast into the cured silicone mold: plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc.
 
Specifications of RTV-2 Silicone Rubber for Soap Mold Making
 
1. Good flow ability and long working time
2. Low hardness, easy de-mold
3. High tear and tensile strength
4. Acid and alkali-resistance
5. Low linear shrinkage
 
Applications of RTV-2 Silicone Rubber for Soap Mold Making
 
MCSIL-215/218 silicone rubber is suited for middle size reproduction of candle mold, soap mold, small size concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, and the products with thin flower patterns.       
 
Detail Standard of RTV-2 Silicone Rubber for Soap Mold Making
 Base and Curing Agent Mixture (100:2 by weight) in 25C (77F) testing

 

 

How to make the silicone mold?
 
1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
 
2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100:2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F).it's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3 to 5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
 
3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.
 
Storage of RTV-2 Silicone Rubber for Soap Mold Making
 
When the silicone rubber is stored at or below 30C (85F) in the original unopened containers, silicone base and curing agent have a usable life of 12 months from the date of production.
 
Note of RTV-2 Silicone Rubber for Soap Mold Making
 
RTV2 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.
 
Packing of RTV-2 Silicone Rubber for Soap Mold Making
 
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum 
Part B CA30 Curing Agent: 0.25kg/bottle,1kg/bottle and 10kg/bottle

Need more information, please feel free to contact Julie.

Item No.	MCSIL-218
Applications	Candle/Soap Molding
Color	Off- white
Curing agent	CA30
Mixing ratio	100:2
Mixed viscosity	22000-23000 cps
Pot life	30-40 Minutes
Curing time	4-6  Hours
Hardness	18-20 Shore A
Tear Strength	25 N/mm
Tensile Strength	≥3.8 Mpa
Shrinkage	0.30%
Elongation at break	520%