Artificial Cultured Stone Casting Liquid Silicone Rubber

• Customization: Available
• Raw Material: Silicone Raw Material
• Material: Silicone Rubber
• Model NO.: MCSIL-2066/2088 silicone
• Appearance: Liquid
• Form: Liquid Rubber
• Item: Mcsil-2066
• Color: off-White
• Mixing Ratio: 100:2
• Hardness: 28-30 Shore a
• Pot Life: 20-30 Mins
• Curing Time: 2-3 Hours
• Tensile Strength: 3.8 MPa
• Tear Strength: 27 N/Mm
• Enlongation: 420%
• Shrinkage: 0.3%
• Transport Package: 20kg/Drum, 25kg/Drum or 200kg/Drum
• Specification: REACH, MSDS, SGS
• Trademark: MC SILICONE
• Origin: Dongguan, China
• HS Code: 39100000
• Production Capacity: 4000kg/Day

Product Description

Description of Cultured Stone Casting RTV-2 Silicone

RTV-2 silicone is a two-component material, this kind of silicone consists of Part A base silicone and Part B CA30 curing agent, and Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone molds: Plaster polyurethane, PU, GRC, cement, resin, polyester, wax etc...

Features of Cultured Stone Casting RTV-2 Silicone

1. Good flowability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage

Applications of Cultured Stone Casting RTV-2 Silicone

MCSIL-2066/2088 silicone is especially suited for reproduction of middle size cement molds, concrete stones, and artificial stones. etc...

Item No.	MCSIL-2066
Color	white
Mixing ratio	100:2
Mixed viscosity	23000-26000 cps
Pot life	20-30 mins
Curing time	2-3  Hours
Hardness	28-30 Shore A
Tear Strength	27 N/mm
Tensile Strength	≥3.8 Mpa
Shrinkage	≤0.3%
Elongation at break	420%

How to make the silicone mold? 

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly. 

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent. 
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen. 

3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold. 

Packing of Cultured Stone Casting RTV-2 Silicone

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle

Storage of Cultured Stone Casting RTV-2 Silicone

When the RTV-2 silicone is stored at or below 30 C (85F) in the original unopened containers, Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production. 

Note of Cultured Stone Casting RTV-2 Silicone

MCSIL-2066/2088 silicone is an industrial product and must not be used in food molding, dental human skin molding applications.