Quality Liquid RTV Silicone Rubber

• Customization: Available
• Raw Material: Silicone Rubber Raw Material
• Material: Silicone Rubber
• Model NO.: MCSIL-H25 silicone rubber
• Form: Liquid Rubber
• Item: Mcsil-H25
• Color: off-White
• Mixing Ratio: 100:2
• Mixed Viscosity: 28000-30000 Cps
• Working Time: 30-40 Mins
• Curing Time: 4-6 Hours
• Hardness: 27-28 Shore a
• Tear Strength: 30 N/Mm
• Tensile Strength: 4.5 Mpa
• Elongation at Break: 511%
• Transport Package: 20kg/Drum, 25kg/Drum or 200kg/Drum
• Specification: REACH, MSDS, SGS
• Trademark: MC SILICONE
• Origin: Dongguan, China
• HS Code: 39100000
• Production Capacity: 4000kg/Day

Product Description

Description of RTV-2 Silicone Rubber

RTV-2 is a two-component Room-Temperature-Vulcanizing (RTV-2) silicone rubber. Depending on its curing mechanism, two types of RTV-2 are available: "condensation" cure type and "addition" cure type. In general, RTV-2 Silicone rubber is a two-component material, and the silicone rubber includes Part A base silicone and Part B CA30 curing agent. The Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These silicone materials can be cast into the cured silicone mold: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...


Features of RTV-2 Silicone Rubber

1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage

Applications of RTV-2 Silicone Rubber

RTV2 Silicone rubber series are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.

Instruction for making silicone mold

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Storage of RTV-2 Silicone Rubber

When the silicone rubber is stored at or below 30C (85F) in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production. After 12 months, please use a stirring mill to stir the Part A silicone for some minutes, then the silicone can be use again, without any influence to the characteristics.

Packing of RTV-2 Silicone Rubber

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle

Need more information, please feel free to contact Nicole.

Item	MCSIL-H25
Color	off-white
Curing agent	CA30
Mixing ratio	100:2
Mixed viscosity	28000-30000 cps
Working time	30-40 mins
Curing time	4-6  Hours
Hardness	27-28 Shore A
Tear Strength	30 N/mm
Tensile Strength	4.5 Mpa
Shrinkage	≤0.3%
Relative density	1.11-1.15g/cm3
Elongation at break	511%