Features of Transparent RTV-2 Molding Silicone Rubber:
1- Transparent RTV-2 Molding Silicone Rubber has an good operability.
2- Transparent RTV-2 Molding Silicone Rubber has good Temperature and deformation resistance as well as low shrinkage.
3- Transparent RTV-2 Molding Silicone Rubber has High duplication times.
Description of Transparent RTV-2 Molding Silicone Rubber:
Transparent RTV-2 Molding Silicone Rubber is generally named as two-part room temperature cure silicone rubber, which features an exceptional fluidity and good operability. When mixed with 10% curing agent, they can still be operated within 60 minutes, but will be formed after 12-24 hours. With resistance to deformation, high temperature, acid and alkali, and expansion.
Storage and Precautions of Transparent RTV-2 Molding Silicone Rubber:
Transparent RTV-2 Molding Silicone Rubber is an environmentally-friendly liquid silicone product, is not easy to burn and can be stored and transported as non-hazardous goods. The shelf life of the product is about one year from the date of production. Inspection is required when exceeding the time limited. It can continue to be used in case of neither thickening nor deterioration.
Package of RTV-2 molding silicone rubber
Part A base silicone: 20kg/drum, or 200kg/drum
Part B CA30 Curing Agent: 1kg/bottle and 10kg/bottle
Professional factory of RTV-2 Molding Silicone:
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series, we are competitive in price with good quality.
Should you have any question, please feel free to contact us.
MINGCHENG GROUP LIMITED
Mob : 008615802546505
Technical parameter of Addition silicone rubber
| Item |
RTV1030 |
| Color |
Transparent |
| Curing agent |
Clear |
| Mixing ratio |
1:1 |
| Mixed viscosity |
4~50k cps |
| Working time |
60 Minutes |
| Curing time (25 Centigrade / h) |
8-12 Hours |
| Curing by heat (60Centigrade/ h) |
1.5 Hours |
| Hardness |
30-35 Shore A |
| Tear Strength |
>20 KN/m |
| Tensile Strength |
4.5 MPA |
| Elongation at break |
>350% |
|