Gypsum Moulding Raw Material Silicone Rubber

Raw Material: Silicone Rubber Raw Material
Material: Silicone Rubber
Appearance: Liquid
Form: Liquid Rubber
Item: Mcsil-H25
Color: off-White
Customization:

Contact Supplier

Gold Member Since 2013

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
MCSIL silicone rubber
Mixing Ratio
100:2
Hardness
27-28 Shore a
Mixed Viscosity
25000-26500 Cps
Working Time
30-40 Mins
Curing Time
4-6 Hours
Tear Strength
30 N/Mm
Tensile Strength
4.5 MPa
Elongation at Break
510%
Transport Package
20kg/Drum, 25kg/Drum or 200kg/Drum
Specification
REACH, MSDS, SGS
Trademark
MC SILICONE
Origin
Dongguan, China
HS Code
39100000
Production Capacity
4000kg/Day

Product Description

Description of Gypsum Mold Making Silicone Rubber Raw Material

Gypsum Mold Making Silicone Rubber is a two-component material, this kind of silicone rubber consists of Part A base silicone and Part B CA30 curing agent, and Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone molds: Plaster polyurethane, PU, GRC, cement, resin, polyester, wax etc...

Features of Gypsum Mold Making Silicone Rubber Raw Material

1. Good flowability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage

Applications of Gypsum Mold Making Silicone Rubber Raw Material

MCSIL-2025/H25/2030 silicone rubber is suitablr for gypsum mold making.

How to make the silicone mold?

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Packing of Gypsum Mold Making Silicone Rubber Raw Material

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle

Storage of Gypsum Mold Making Silicone Rubber Raw Material

When the RTV-2 silicone rubber is stored at or below 30 C (85F) in the original unopened containers, Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production.

Note of Gypsum Mold Making Silicone Rubber Raw Material

RTV2 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.

Should you have any question, please feel free to contact us.

 
Mob: 008615802546505
 
 
ItemMCSIL-H25
Coloroff-white
Curing agentCA30
Mixing ratio100:2
Hardness27-28 Shore A