High clear Liquid Silicone molding rubber
High clear Liquid Silicone molding rubber application:
Molding silicone rubber is suitable for product duplication and molds manufacture such as
1) Toys, gifts
2) Decoration, plate engrave
3) Human replica, art crafts,
4) Resin crafts, unsaturated resin crafts
5) Poly resin crafts, candle crafts, plastic crafts
6) Stationeries, plaster crafts, Buddhist statue crafts, etc.
High clear Liquid Silicone molding rubber features:
a. good characteristics of easy-operation
b. light viscosity and good flow ability
c. favorable tension
d. low shrinkage
e. no deformation
f. high temperature resistance, acid and alkali-resistance and ageing resistance
Advantage of High clear Liquid Silicone molding rubber:
Molding silicone rubber has advantage of excellent fluidity and good operational performance; an elastic silicone rubber mold will be obtained with resistance to deformation, high-temperature, acid and alkali and expansion, comfortable duplication times and free sample available.
High clear Liquid Silicone molding rubber specifications:
Hardness ranging from 10 to 60 shore A;
Viscosity varies from 9000 to 80000 cps.
High clear Liquid Silicone molding rubber operations:
Molding silicone rubber is a kind of flowing liquid, and it consists of two components, part A is a flowable liquid silicone rubber, part B is the curing agent.
Firstly, after your previous work of dealing with the original model, take some liquid silicone rubber, add 2%~3% cuing agent of the amount of silicon and mix them evenly.
Then after vacuum-pumping the mixture, you can pour it into the mold frame. The silicone mold will cured in 2~3 hours.
Notes of High clear Liquid Silicone molding rubber operations:
The time for vacuum-pumping should be less than 3-5 mins, otherwise, once the silicone rubber has cross-link reaction during vacuumizing, it will not be operated.
High clear Liquid Silicone molding rubber with FAQ:
Why does the mold made of silicone rubber have an unsmooth surface with tracks and strips on it?
It is due to product or model to be molded should hasn't been sanded or polished . If the mold or product is not sanded or polished, the mold made of whatever quality silicone rubber will not be good and smooth enough since the mold or the product itself is not smooth or perfect. Another case is that uneven brushing of the release agent will also bring about unsmoothness of the mold.
Need more information, please feel free to contact Nicole.
| Item |
MCPLA-H40 |
| Color |
clear |
| Curing agent |
CA30 |
| Mixing ratio |
100:10 |
| Hardness |
40 Shore A |
| Tear Strength |
27 N/mm |
| Tensile Strength |
6 Mpa |
| Shrinkage |
≤0.1% |
| Elongation at break |
360% |
| Relative density |
1.1 g/cm3 |