Fast Cure Silicone Putty for Resin Crafts Molds Making Kneading Silicone Impression Putty

• Customization: Available
• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Model NO.: MC-SP40 A/B
• Form: Powdered Rubber
• Item No.: Mc-Sp40 Silicone Putty
• Mix Ratio: 1:1
• Hardness (Shore a): 40~45 Shore a
• Pot Life (Mins): 2~3 Mins
• Curing Time (Hrs): 20-30 Mins
• Tensile Strength(MPa): 2.5
• Elongation Break: 350%
• Shrinkage: 0.1%
• Shelf Life: 12 Months
• Transport Package: Plastic Can
• Specification: 350g, 500g, 1kg, 5kg, 10kg, 25kg
• Trademark: MC silicone
• Origin: China, Guangdong
• HS Code: 39100000
• Production Capacity: 800kg/Day

Product Description

Fast Cure Silicone Putty for Resin Crafts Molds Making Kneading Silicone Impression Putty

Introduction
MC- Silicone PUTTY is a hydrophilic addition silicone rubber impression material, it contains two components, Part A is platinum catalyst, and Part B is hydrogen containing polysiloxane. This product comprises liquid material and powder material. The main raw material is a silicone oil, silicone resin, alumina, quartz powder and etc.

 

Features:
-Easy to use, 3 Minute working time, 25 minute cure.
-Ideal for small molds, excellent detail from original.
-Strong, flexible, reusable molds.
-High Heat range, up to 400°F.
-No Shrinkage.
-Self releasing, no mold release agent required for most applications.
-Odorless, Non Toxic. Skin safe.

Application
Applications include making fast mold impressions from almost any surface, miniatures, toys, chocolate & candy, orthotics / orthopedic, equine hoof repair, jewelry mold making, resin crafts, etc.
 

Physical Properties:

 

Before Curing	Catalyst Components	Base Components
Appearance	White putty	Blue putty
Mix ratio	1:1
Pot life	3-5 minutes
Curing time(37C)	<30 minutes
After Curing
Hardness(Shore A)	25
Permanent deformation %	<0.2%
Dimensional stability %	<0.25
Copy details(μm)	<1.5
tensile Strength Mpa	2.5
Temperature stability	60°C for 1 week
Elongation%	350

Usage Instruction

 

1. Under the room temperature, take the same amount of base component (blue) and catalyst component (white).

 

2. Mix the two components together. It is recommended to use the blue spoon to take the base component and white spoon to take catalyst  component.

 

3. Use your fingertips to mix the two components together and knead for at least 30 seconds until they are mixed completely.

 

4. Close the lid immediately after usage, the cover can not be interchanged.

Package

Package available in 350g, 500g, 1kg,5kg,10kg,15kg,20kg,25kg. Sample is available in 100gA+100gB.

Storage

Silicone Impression Putty has a shelf life of 12 month in original package at a cool dry place.

 

Precautions

1. Do not use natural rubber gloves. Silicone Impression Putty is recommended to use disposable polyethylene plastic gloves.

2. Silicone Impression Putty contains platinum catalyst, sulfur, phosphorus, amine, etc. will slow down or even stop the curing reaction, and thus it must avoid sulfur, phosphorus, amine, acrylic and meth acrylic acid esters and other chemical products in use.

3. Close the lid tightly and immediately after use, keep Silicone Impression Putty in cool place, and be refrigerated in summer.

4. The temperature has a significant impact on the curing time; the curing reaction will slow down at low temperature, and speed up at high temperature curing speed. It should adjust operation rhythm according to the environment and the finger temperature.

5. Silicone Impression Putty is strictly recommended to use the same amount of base and catalyst. Unequal amount will lead to delayed or accelerated cure.

[email protected]