RTV-2 Mold Making Rubber Silicone for Roman Gypsum Column Mouldmaking
Description of RTV-2 Mold Making Rubber Silicone for Roman Gypsum column mouldmaking
RTV-2 Silicone is a two-component material, and the silicone rubber includes Part A base silicone and Part B CA30 curing agent. The Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These silicone materials can be cast into the cured silicone mold: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...
Features of RTV-2 Mold Making Rubber Silicone for Roman Gypsum column mouldmaking
1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
Applications of RTV-2 Mold Making Rubber Silicone for Roman Gypsum column mouldmaking
RTV-2 Silicone are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.
How to make the silicone mold?
1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35° C (95° F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.
Storage of RTV-2 Mold Making Rubber Silicone
When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
RTV2 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.
| Item |
MCSIL-H25 |
| Color |
white |
| Mixing ratio |
100:2 |
| Mixed viscosity |
25000-26500 |
| Working time |
30-40 mins |
| Curing time |
4-5 Hours |
| Hardness |
27-28 Shore A |
| Tear Strength |
30 N/mm |
| Tensile Strength |
4.5 Mpa |
| Shrinkage |
≤0.3% |
| Elongation at break |
510% |
Package of Mold Making Silicone Rubber RTV 2 To Pouring Grc Gypsum Mould
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle and 1kg/bottle
Professional factory of RTV2 silicone:
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series, we are competitive in price with good quality.
Should you have any question, please feel free to contact us .