White Tin Cured Silicone RTV2 Liquid Silicone Molding Rubber

• Customization: Available
• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Model NO.: MCSIL-2020, RTV2020
• Appearance: Liquid White
• Form: Liquid Rubber
• Curing Agent: Tin Catalyst
• Color: White Silicone Molding Rubber
• Mix Ratio: 2% Catalyst
• Viscosity: 22000 Cps
• Pot Life: 30-40 Mins
• Curing Time: 4-6 Hrs
• Hardness: 20 Shore a
• Tensile Strength: 3.8 MPa
• Tear Strength: 30n/mm
• Elongation: 550%
• Shrinkage: 0.3%
• Shelf Life: 12months
• Transport Package: 25kg, 200kg
• Specification: MSDS, REACH
• Trademark: MC Silicone
• Origin: Dongguan
• HS Code: 39100000
• Production Capacity: 8000kg Per Day

Product Description

Product Description

MCSIL-20series RTV2 silicone rubber is a kind of two-component material, that is the mold making silicone rubber made up of Part A base silicone and Part B curing agent. The mixed Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction,thenbecome a silicone rubber mold that can be used for objects reproduction.

Product Parameters

Item no.	RTV 2020
Color	white/translucent
Viscosity	20000±2000 cps
Mix ratio	100:2
Pot life	30-40 mins
Curing time	4-6 hrs
Hardness	20 shore A
Tensile strength	3.8 Mpa
Elongation	550%
Tear Strength	30 N/mm
Shrinkage	0.3%

Features

Advantages of  tin cured liquid rtv2 silicone rubber:
#Amazing fluidity and easy to operate Complex design available

#Not Oily ,Stable quality

#catalyst provided

#Easy de-molding 

#Excellent tension and tear strength

#High performance in duplication

#Shrinkage is almost zero (below 0.3)

#Excellent resistance to weather, temperature, aging, acid and aging-proofing.

Applications

Various apppications of  tin cured liquid rtv2 silicone rubber:

1- Liquid RTV2 Silicone for making moulds for plaster decorations like cornice, corbel, ceiling dome

2- Liquid RTV2 Silicone for making moulds for Cultural relic duplication, architectural decoration

3- Liquid RTV2 Silicone for making moulds for Polyester/Polyurethane/Epoxy Resin crafts 

4- Liquid RTV2 Silicone for making moulds for Lighting ornaments, candles 

5- Liquid RTV2 Silicone for making moulds for Concrete decorations like artificial stone, column

6- Liquid RTV2 Silicone for making moulds for soap, candle, wax, etc.
 

Installation Instructions

How to use tin cured liquid silicone to make mold? 

The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
 Mixing

Please weight 100 Part A base and 2 parts of Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in
the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent. It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
2.Pouring the mixture and curing

Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Shelf Life and Storage

When stored at or below 30 C (85F) in the original unopened containers, silicone base and CA30 Curing agent have a usable life of 12 months from the date of production. After 12 months stock, please use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again, no influence for other performances. 

Packaging & Shipping

Packing of  tin cured liquid rtv2 silicone rubber:

20kg/drum, 25kg/drum or 200kg/drum of silicone rubber Part A
0.8kg/bottle, 1kg/bottle of silicone rubber Part B