DESCRIPTION of White Liquid Silicone Rubber
White Liquid Silicone Rubber for Making Molds is generally named as two-part silicone rubbers which vulcanise, or cure, at room temperature. Part A is a dynamic liquid silicone/Part B is the curing agent (tin catalyst).
APPLICATIONS of White Liquid Silicone Rubber
White Liquid Silicone Rubber for Making Moldscan be used for construction of moulds for gypsum, soap, candles, concrete, resin products, artificial (very lightweight) stone, wax or custom moulds;
White Liquid Silicone Rubber for Making Molds can be used for making decorative building moulds (cornice, column, balustrade, ceilling roses, pedestals, fountains, mantels, wall ornament, planter etc;
ADVANTAGES of White Liquid Silicone Rubber
Exceptional fluidity and good operability, easy to demold.
Cures at room temperature within 3-4 hours (assuming constant temp of 25 degrees C).
Good tensile and tear strength, low shrinkage (<0.3%)
High duplication levels or longevity
Good resistance to weather, temperature, aging, acid.
Long shelf life (12 months at least) if kept at constant temperatures.
STORAGE of White Liquid Silicone Rubber
Two Components Mold Making Silicone Rubber is an environmentally-friendly liquid silicone product, is not easy to burn and can be stored and transported as non-hazardous goods. The shelf life of the product is about
12 months from the date of production. Inspection is required when exceeding the time limited. It can continue to be used in case of neither thickening nor deterioration.
PACKAGING of White Liquid Silicone Rubber
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle, 1kg/bottle
COMPANY INFORMATION
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series, we are competitive in price with good quality.
Need more information , please contact us freely .
| Item no. |
MCSIL-H20 |
| Color |
white |
| Viscosity |
25000±2000 cps |
| Mix ratio |
100:2 |
| Pot life |
30-40 mins |
| Curing time |
4-6 hrs |
| Hardness |
20 shore A |
| Tensile strength |
3.8 Mpa |
| Elongation |
600% |
| Tear Strength |
30 N/mm |
| Shrinkage |
0.3% |