Introduction of RTV-2 Silicone Rubber For GRC Mold Making
RTV-2 is a two-component Room-Temperature-Vulcanizing (RTV-2) silicone rubber. Depending on its curing mechanism, two types of RTV-2 are available: "condensation" cure type and "addition" cure type. Generally, RTV-2 Silicone Rubber is a kind of two-component material. The RTV-2 silicone rubber is made up of Part A base silicone and Part B curing agent. The Part A base silicone and Part B CA curing agent can cure at room temperature by a condensation reaction, after full cure, it become a cured silicone mold. The silicone mold can be cast the following materials for reproduction: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...
Characteristics of RTV-2 Silicone Rubber For GRC Mold Making
1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
Applications of RTV-2 Silicone Rubber
RTV-2 silicone rubber can be applied in many objects mold making, since the RTV-2 silicone has good flow ability and medium hardness, and the silicone can cure at room temperature, thus it's a good material for duplication.
RTV-2 Silicone Rubber can be used for artificial stone moldmaking. For example MCSIL-2066 and MCSIL-2088 silicone.
RTV-2 silicone rubber can be appliied in candle and soap moldmaking, such as MCSIL-215 and MCSIL-218 silicone.
RTV-2 silicone rubber can be used for plaster moldmaking, such as MCSIL-2025, MCSIL-H25 and MCSIL-2030 silicone.
RTV-2 silicone rubber can be applied in the field of shoe sole moldmaking, for example, MCSIL-S10 and MCSIL-S15 silicone.
RTV-2 silicone rubber can be used for prototyping and electronic potting.
MCSIL-2030 silicone rubber is suitable for plaster and GRC mold making.
How to make the silicone mold?
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.
Storage of RTV-2 Silicone Rubber For GRC Mold Making
When the RTV-2 silicone rubber is stored at or below 30 C (85F) in the original unopened containers, Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production.
Note of RTV-2 Silicone Rubber For GRC Mold Making
MCSIL-2030 silicone rubber is an industrial product and must not be used in food molding, dental human skin molding application.
Need more information, please feel free to contact Nicole
| Item |
MCSIL-2030 |
| Color |
white |
| Mixing ratio |
100:2 |
| Mixed viscosity |
20000-23000 cps |
| Working time |
30-40 Minutes |
| Curing time |
4-6 Hours |
| Hardness |
28-30 Shore A |
| Tear Strength |
30 N/mm |
| Tensile Strength |
3.8 MPA |
| Shrinkage |
≤0.3% |
| Elongation at break |
480% |