Brief Introduction of High Strength Mold Making RTV-2 Silicone Rubbers :
High Strength Mold Making RTV-2 Silicone Rubbers is generally named two-components silicone rubber, Part A is a flowable liquid, part B is the curing agent. It features an exceptional fluidity and good operability. The mixing ratio is 100:2,mainly be suitable for making stone molds application.
Mainly application of High Strength Mold Making RTV-2 Silicone Rubbers :
High Strength Mold Making RTV-2 Silicone Rubbers is a two part silicone rubber and curing with tin catalyst. As with a low viscosity,high tear strength and excellent duplication times,it's widely used for concrete casting,cement products casting,Making silicone rubber molds for artificial stone,concrete crafts,cement crafts,GRC/GPR decorations casting.
Features of High Strength Mold Making RTV-2 Silicone Rubbers :
a.low viscosity
b.easy operation
c.long shelf life over 12 months
d.high strength and low shrinkage
e.curing at room temperature within 4-6 hours
f.high duplication times and no deformation
How to making stone mold with rtv2 silicone rubber?
Mixing:
Select a mixing container 4-5 times larger than the total volume of material to be mixed.
Weigh out the selected silicon rubber and catalyst. Stir for several minutes scraping the
sides and bottom of the container carefully to produce a homogeneous mixture. When
using power mixers, avoid excessive speeds, which could entrap large amounts of air or
cause overheating of the mixture, resulting in shorter pot life.
The air entrapped in the mixing step needs to be removed to eliminate voids in the cure
product. This can be done by exposing the material to a vacuum of 10-20 mbar. The
material will expand, crest and reduce to about the original level. Degassing is usually
complete about two minutes after frothing ceases.
Curing:
After mixing the two parts combination, the material will cure at room temperature. Selection of the Beta will determine cure speed, the work life as well as the demoulding time.
The system is sensitive to changes in heat and humidity and therefore variations in cure
speed may be seen if one or both variables are changed.
Package of High Strength Mold Making RTV-2 Silicone Rubbers:
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle, 1kg/bottle
Professional factory of High Strength Mold Making RTV-2 Silicone Rubbers:
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series, we are competitive in price with good quality.
Should you have any question, please feel free to contact Ms Julie.
MINGCHENG GROUP LIMITED
){kind=link}
){kind=link}