Liquid Silicone Rubber for Sculpture Mould Making
Introduction of Sculpture Mould Making Liquid Silicone Rubber
RTV-2 is a two-component Room-Temperature-Vulcanizing (RTV-2) silicone rubber. Depending on its curing mechanism, two types of RTV-2 are available: "condensation" cure type and "addition" cure type. Generally, RTV-2 Silicone Rubber is a kind of two-component material. The RTV-2 silicone rubber is made up of Part A base silicone and Part B curing agent. The Part A base silicone and Part B CA curing agent can cure at room temperature by a condensation reaction, after full cure, it become a cured silicone mold. The silicone mold can be cast the following materials for reproduction: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...
Specifications of MC Liquid Silicone Rubber
Room Temperature Vulcanization
Equipped with REACH certificate
Professional technician with rich experience
4% catalyst offers for free of charge
Silicone hardness range: 10-60 shore A
High duplicating silicone molds
Characteristics of Sculpture Mould Making Liquid Silicone Rubber
1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
Applications of Liquid Silicone Rubber
Liquid silicone rubber for mold making can be used in the filed of reproducing cement molds, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.
Liquid silicone rubber can be applied in many objects mold making, since the RTV-2 silicone has good flow ability and medium hardness, and the silicone can cure at room temperature, thus it's a good material for duplication.
RTV-2 Silicone Rubber can be used for artificial stone moldmaking.For example MCSIL-2066 and MCSIL-2088 silicone.
RTV-2 silicone rubber can be appliied in candle and soap moldmaking, such as MCSIL-215 and MCSIL-218 silicone.
RTV-2 silicone rubber can be used for plaster moldmaking, such as MCSIL-2025,MCSIL-H25 and MCSIL-2030 silicone.
RTV-2 silicone rubber can be applied in the field of shoe sole moldmaking, for example, MCSIL-S10 and MCSIL-S15 silicone.
RTV-2 silicone rubber can be used for prototyping and electronic potting.
MCSIL-H25/2030 silicone rubber can be also used for sculpture mold making.
Procedures of Liquid Silicone Rubber
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Need more information, please feel free to contact Nicole.
| Item |
MCSIL-H25 |
| Color |
off-white |
| Curing agent |
CA30 |
| Mixing ratio |
100:2 |
| Hardness |
27-28 Shore A |
| Tear Strength |
30 N/mm |
| Tensile Strength |
4.5 Mpa |
| Shrinkage |
≤0.3% |
| Relative density |
1.11-1.15g/cm3 |
| Elongation at break |
511% |
){kind=link}